The local environment of Co2+ ions intercalated in vanadium oxide/hexadecylamine nanotubes.

Vanadium oxide nanotubes constitute promising materials for applications in nanoelectronics as cathode materials, in sensor technology and in catalysis. In this work we present a study on hybrid vanadium oxide/hexadecylamine multiwall nanotubes doped with Co ions using state of the art x-ray diffraction and absorption techniques, to address the issue of the dopant location within the nanotubes' structure. The x-ray absorption near-edge structure analysis shows that the Co ions in the nanotubes are in the 2 + oxidation state, while extended x-ray absorption fine structure spectroscopy reveals the local environment of the Co(2+) ions. Results indicate that Co atoms are exchanged at the interface between the vanadium oxide's layers and the hexadecylamines, reducing the amount of amine chains and therefore the interlayer distance, but preserving the tubular shape. The findings in this work are important for describing Co(2+) interaction with vanadium oxide nanotubes at the molecular level and will help to improve the understanding of their physicochemical behavior, which is desired in view of their promising applications.

Hybrid particles of polystyrene and carboxymethyl cellulose as substrates for copper ions.

The synthesis of hybrid particles was carried out by emulsion polymerization of styrene in complexes formed by carboxymethyl cellulose (CMC), a polyanion, and a cationic surfactant, cetyltrimethylammonium bromide (CTAB). CMC chains with variable molecular weights and degrees of substitution were tested. The polymerization condition chosen was that corresponding to CMC chains fully saturated with CTAB and to the onset of pure surfactant micelle formation, namely, at the critical aggregation concentration. The hybrid particles were characterized by zeta potential and light scattering measurements. The period of colloidal stability in the ionic strength of 2.0 mol L(-)(1) NaCl was observed visually. Upon increasing the CMC chain length, the particle characteristics remained practically unchanged, but the colloid stability was increased. The increase in the CMC degree of substitution led to particles with more negative zeta potential values. The adsorption of copper ions (Cu(2+)) on the surface of hybrid particles could be described by the Langmuir model, as determined by potentiometric measurements. The increase in the mean zeta potential values and X-ray absorption near-edge spectra evidenced the immobilization of Cu(2+) ions on the hybrid particles.